A7 TOP Neutral Silicone S
A7 TOP - Neutral Silicone S
SILSEAL-WNDWCNST-(A7 TOP)-S-WHTE-310ML
Register now and access more than 125,000 products
- Suitable for sanitation applications
- Very good adhesion to most common glazes and paints, as well as on glass, tiles, ceramics, aluminium, steel, zinc, copper and many plastics
- Permanently elastic
- Resistant to ageing, weathering and UV
- Compatible with paint
- Low stringing
- Does not have a tacky surface
- Not corrosive to metals
- Can be used on alkaline substrates such as concrete, mortar and fibre cement
- Almost odourless, free of organic plasticisers, therefore low volume shrinkage and stable
This information is only a recommendation based on our experience. Preliminary testing is required.
Complies with DIN 18545-E and ISO 11600 F+G, class 25 LM, and SNJF glazing and façades, class 25E.
Datasheets(X)
For sealing joints exposed to high moisture, e.g. in sanitary areas, for glazing and window sealing of expansion joints in wooden, plastic and aluminium windows. Sealing joints between glazing units and load components (frames, beams, posts). Also suitable for connection, expansion and sealing joints indoors and outdoors. Suitable for cold climates.
The base material must be clean, dry and load-bearing. Note the joint size. Prime the joints with backer rod, art. no. 0875... Treat porous substrates with silicone primer, Art. no. 0892 170. Before the skin forms, smooth with sealant smoothing agent, Art. no. 0893 3/0893 003.
Container | Cartridge |
Contents | 310 ml |
Chemical basis | Neutrally networked silicones, with alkoxy basis (alcohol basis) |
Colour | White |
Density | 1.02 g/cm³ |
Continuous motion absorption | 25 % |
Min./max. processing temperature | 5 to 40 °C |
Min./max. temperature resistance | -40 to 180 °C |
Full curing speed/conditions | 2 mm/d / 23°C and 50% relative humidity |
Min. breaking elongation | 300 % |
Building material class/conditions | B2 - Normally inflammable / in accordance with DIN 4102-4 |
Shelf life from production | 12 Month |